Performance of high-speed ball bearings with lead-plated retainers in liquid hydrogen for potential use in a radiation environment /
Donald W. Wisander, David E. Brewe, and Herbert W. Scibbe.
Description
- Language(s)
-
English
- Published
-
Washington, D.C. : National Aeronautics and Space Administration : 1972.
- Summary
-
Ball bearings (40-mm bore) with lead coated, aluminum-bronze retainers were operated successfully in liquid hydrogen at 30,000 rpm under a thrust load of 1780 newtons (400 lb) for running times up to 15 hours. The lead transfer films on the bearing surfaces prevented galling of bearing components. The lead coated retainers used in this investigation show promise for use in the high radiation environments, where polytetrafluoroethylene (PTFE) based materials are not suitable. Failure was a result of the loss of lead lubricant on the retainer-inner-land and ball-pocket surfaces. The longest bearing life (15 hr) was achieved with a lead coating thickness of 50 micrometers (0.002 in.) on the retainer. Other bearings had lives of 2 to 6 hours.
- Physical Description
-
12 p. :
ill. ;
27 cm.
Viewability
| Item Link |
Original Source |
|
Full view
|
University of Illinois at Urbana-Champaign
|